92% 高密度化されたシリカフューム

SiO₂: >92%
色: Grey
PH Value: 6~8
かさ密度: 200~350kg/m3, 550~650kg/m3, Above 700kg/m3
Packages:1000kg plastic woven bags, 10kgの可溶性紙袋, 20kgの可溶性紙袋, 25kg plastic woven bags, 500kg plastic woven bags, 600kg plastic woven bags, 950kg plastic woven bags

序章

92% Densified Silica Fume is a micro-silica fume with 92% SiO2含有量, and the Bulk density is 250-400kg/m³.

Densified Silica Fume is to improve the density of micro-silica fume in order to reduce the transportation cost and improve the use performance. Before Densified, its density is about 150 に 200 kg/m³, after densified, それは到達することができます 700 kg/m³, これにより、体積が大幅に減少し、同時に粒子サイズが改善されます. The densified process used nowadays is to use the airflow formed by compressed air to prompt the micro-silica fume in the container to collide with each other and rely on its own aggregation and adsorption to exclude the surface gas, thus forming multiple small particles with increased capacity to achieve the purpose of densified.

利点

コンクリートの浸透性を下げる

コンクリートの耐久性を大幅に向上

究極の強さの増加

あらゆるタイプの高強度コンクリート用途に有益

鋼への接着強度を向上させます

アルカリシリカ反応性を大幅に低下させます

硫酸塩または海水の攻撃に対する優れた耐性を提供します

鋼の腐食を低減します

パラメーター

スリカスモーク	結果
SiO₂ (%)	96
水分 (%)	0.46
Na₂Oなどのアルカリ (%)	0.47
遊離 CaO (%)	0.09
と (%)	0.12
無料CI% (%)	0.002
SO₃ (%)	0.2
L.O.I (%)	3.7
比表面積 (mg)	22
サイズ	0.14
加速されたポゾラン活動 ( 7 日々 )	126

アプリケーション

水の保全と水力工学: 浸透防止および摩耗防止部品, マイクロシリカ粉末と混合した後, 浸透防止を大幅に改善できます, ひび割れ防止, 耐摩耗性と耐キャビテーション性能.
高強度コンクリートの製造: 高強度コンクリートを製造するための混和剤としてのシリカ粉末, その強度レベルの実際の適用は100Mpaを達成することができます.
海港工学: シリカ粉末と混合されたコンクリートは、コンクリートの耐摩耗性能を向上させることができます, 浸透防止性能, 鉄筋の電気化学的腐食を防ぐため.
交通工学: 高速道路の舗装や航空機の滑走路に使用されるシリカ粉末コンクリート, コンクリートの初期強度と耐摩耗性を大幅に向上させることができます, 高速道路舗装のメンテナンスと修理, 開店時間を早め、経済的利益を増やすことができます.
吹き付けコンクリート: プラスチックコンクリートの接着性能と凝集力を大幅に向上, リバウンド量を大幅に削減, 形成された吹付けコンクリートの厚さを増やす, 建設期間を短縮し、プロジェクトのコストを節約します.