구체적인 준비 과정에서, 미네랄 혼화제는 콘크리트의 성능을 향상시키는 데 필요한 혼합 재료입니다.. Commonly used mineral admixtures include 플라이 애쉬, 슬래그 분말, 등., but in high-strength concrete, silica fume is also a must. 미네랄 혼화제, fly ash and silica fume are admixtures containing a large amount of silica, is it possible to replace fly ash with silica fume? 다음, I will tell you whether silica fume can replace fly ash through the comparison between silica fume and fly ash.

Performance comparison between silica fume and fly ash

Liquidity comparison

(1) Natural mobility

Put a steel pipe with a height of 18cm and a diameter of 7cm on a flat plastic paper, and slowly lift the steel pipe after it is freely filled with silica fume, and measure the free fall fluidity of the silica fume. The diameter is 20cm, and the center height is 7cm; use the same device And method, measured fly ash free fall fluidity diameter is 28cm, center height is 3.5cm. It can be seen that the diameter of the free flow of silica fume is 8cm smaller than that of fly ash, and the height of the center is 3.5cm. The natural flow of silica fume is smaller than that of fly ash.

(2) Slurry fluidity

Experiments were carried out on the fluidity of silica fume and fly ash cement (according to the determination method of fluidity of cement slurry), and the fluidity of cement slurry mixed with 3% 그리고 5% silica fume was measured to be 220mm and 210mm respectively; The fluidity of cement paste with 3% 그리고 5% fly ash is 220mm and 220mm respectively. It can be seen that the fluidity of the cement slurry mixed with 3% silica fume is the same as that of the cement slurry mixed with 3% 플라이 애쉬, and the fluidity of the cement slurry mixed with 5% silica fume is lower than that of the cement slurry mixed with 5% 플라이 애쉬. Spend.

Comparison of cement performance under the same proportion

1. Adding silica fume in the same proportion requires less water than the standard consistency of fly ash, but with the increase of silica fume content, the water consumption of standard consistency increases.
2. The initial setting time and final setting time of fly ash mixed with the same proportion are prolonged, and the setting time is further prolonged with the increase of silica fume content.
3. With the addition of silica fume in the same proportion, the 3d and 28d compressive strengths of fly ash both increase, but with the increase of silica fume content, the increase rate of cement strength shows a downward trend.

Read More About Silica Fume and Fly Ash Visit: https://hsamaterial.com/blog/silica-fume-vs-fly-ash.html

Feasibility of silica fume replacing fly ash in the same proportion

After testing, it is found that when the same proportion of silica fume is used instead of fly ash, the fluidity loss of concrete increases, and the workability of construction becomes poor. 하지만, since silica fume fills the voids of concrete, the amount of mixing water decreases, and the strength of concrete at 7d and 28d Both increased, indicating that silica fume can improve the strength of concrete by replacing fly ash.

Since the initial setting and final setting time will be prolonged after the addition of silica fume, it is not suitable for preparation and use in seasons with low temperatures, and the silica fume is finer and has a smaller bulk density. 저장, feeding stability and admixture should be considered when using it. According to the test data, the appropriate dosage of silica fume as an admixture is 3%, which can reduce water demand and improve early and late strength.

요약하자면, under certain conditions, 실리카흄 can be added to cement or concrete instead of fly ash, 하지만 실제 사용시, the actual amount of silica fume added should be determined through a reasonable ratio test, and most In some cases, in order to improve the performance of concrete in many engineering projects, 실리카흄, fly ash and other admixtures are used in combination.

Henan Superior Abrasives Co.의 마이크로 실리카 흄, 주식회사

이상으로 20 수년간 마이크로 실리카 퓸 제조, Henan Superior Abrasives Co., Ltd는 귀하가 제안한 공급 업체로 자신을 제시합니다.. 중국산 고성능 실리카 제품을 공급하고 있습니다.. Your requirement for densified and undentified silica fume can be fulfilled in different configurations. 프로젝트 요구사항 공유, 그리고 우리는 귀하의 맞춤형 요구 사항을 제공 할 것입니다. 중국에 있는 당사 공장은 요청 시 다양한 실리카 흄 구성을 제공할 수 있습니다..

맞춤형 1000kg 플라스틱 직조 백과 10kg 및 20 kg 가용성 종이 봉투. 플라스틱 짠 가방은 소량 공급도 가능합니다.. 우리의 높은 표준 재료는 전 세계의 다양한 프로젝트에서 사용되고 있습니다.. 우리는 신속한 서비스로 최고의 재료를 제공하기 위해 최선을 다하고 있습니다..