96% 未致密硅粉

二氧化硅: >96%
颜色: 深灰色, Grey
PH Value: 6~8
体积密度: 200~350kg/m3, 550~650kg/m3, Above 700kg/m3
Packages:1000kg plastic woven bags, 10公斤水溶纸袋, 20公斤水溶纸袋, 25kg plastic woven bags, 500kg plastic woven bags, 600kg plastic woven bags, 950kg plastic woven bags

介绍

96% Undensified Silica Fume is a micro-silica fume with 96% 二氧化硅含量, and the Bulk density is 250-400kg/m³.

Silica fume has been used to improve refractory materials for more than 40 年. Silica fume used in refractory materials will have the following characteristics:

1. Improve the flowability of pouring refractory, reduce water consumption, 使其易于成型, 并大大提高生产效率;

2. Due to the intercalation effect of its ultrastructure, the compactness and strength of refractories are greatly improved;

3. Silica fume has high activity, and under the premise of the presence of Al2O3 components, it is easier to generate Mullite phase, which makes the high-temperature strength and thermal shock of refractory material significantly improved.

优点

降低混凝土渗透性

显着提高混凝土耐久性

增加极限力量增益

有益于所有类型的高强度混凝土应用

提高与钢的结合强度

显着降低碱硅反应性

提供出色的抗硫酸盐或海水侵蚀能力

减少钢铁腐蚀

参数

SLICA FUME	结果
二氧化硅 (%)	96
水分 (%)	0.46
Alkalis like Na₂O (%)	0.47
游离氧化钙 (%)	0.09
Si (%)	0.12
Free CI% (%)	0.002
SO₃ (%)	0.2
L.O.I (%)	3.7
比表面积 (mg)	22
尺寸	0.14
Accelerated PozzolanicActivity ( 7 天 )	126

应用

水利水电工程: 在防渗、抗磨损部位, 与微硅粉混合后, 可以大大提高防渗, 抗裂, 抗磨损和抗气蚀性能.
高强混凝土的生产: 硅粉作为外加剂制备高强混凝土, 实际应用其强度等级可达到100Mpa.
海港工程: 掺入硅粉的混凝土可提高混凝土的抗磨性能, 防渗性能, 防止钢筋电化学腐蚀.
交通工程: 用于高速公路路面和飞机跑道的硅粉混凝土, 可大大提高混凝土的早期强度和耐磨性, 在公路路面的养护和维修中, 可以提前开放时间，增加经济效益.
喷射混凝土: 显着提高塑性混凝土的粘附性能和内聚力, 大幅减少反弹量, 一旦形成，增加喷射混凝土的厚度, 缩短工期，节约工程成本.